Download or read book ETUDE DU DEPOT DE FILMS MINCES DE SILICE PAR PLASMA MULTIPOLAIRE MICROONDE. APPLICATION A L'ETUDE DE STRUCTURES SIO#2-INP written by FRANCOIS.. PLAIS and published by . This book was released on 1991 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: LE TRANSISTOR A EFFET DE CHAMP A GRILLE ISOLEE (MISFET) SUR INP EST LE COMPOSANT SUSCEPTIBLE DE REPONDRE AUX SPECIFICATIONS REQUISES DANS LE DOMAINE DE L'AMPLIFICATION HYPERFREQUENCE. LA REALISATION DE CE COMPOSANT PASSE PAR LA MAITRISE DU DEPOT DE SILICE SUR INP ET LA REALISATION D'UNE INTERFACE SANS DEFAUTS. LES TECHNIQUES HABITUELLES DE DEPOT D'ISOLANT (DEPOT ASSISTE PAR PLASMA RADIOFREQUENCE, TEMPERATURE DE SUBSTRAT 250C) INDUISENT DES DEFAUTS DANS LE SUBSTRAT QUI NUISENT A LA QUALITE DU COMPOSANT REALISE. A TITRE D'ALTERNATIVE AUX PLASMAS RADIOFREQUENCES, NOUS AVONS UTILISE UN PLASMA MULTIPOLAIRE MICROONDE POUR DEPOSER LE FILM DE SILICE. LE PLASMA EST CREE, A BASSE PRESSION (10##3 MBAR), DANS UN MELANGE SIH#4-N#2O, PAR RESONANCE CYCLOTRONIQUE ELECTRONIQUE REPARTIE (RCER). LES FILMS OBTENUS A TEMPERATURE AMBIANTE PRESENTENT UNE FAIBLE CONTAMINATION (2 AT% D'AZOTE ET 5 AT% D'HYDROGENE MESURE PAR MICROANALYSE NUCLEAIRE), UNE FAIBLE VITESSE DE GRAVURE HUMIDE (3 FOIS CELLE DE LA SILICE THERMIQUE) ET UNE BONNE RESISTIVITE (10#1#5CM). NOUS AVONS ENSUITE CARACTERISE L'INTERFACE ENTRE LE FILM DE SILICE ET L'INP PAR SPECTROSCOPIE DE PHOTOELECTRONS (XPS) SUR DES COUCHES MINCES OU PAR ANALYSE I(V)-C(V) SUR DES COUCHES EPAISSES. ON MONTRE PAR XPS QUE LE DEPOT DE SILICE OXYDE FORTEMENT LE SUBSTRAT D'INP. LE CHAMP CRITIQUE, POUR LEQUEL LA DENSITE DE COURANT DE FUITE EST INFERIEURE A 1 NA CM##2, DEPASSE 5 MV CM##1, RESULTAT COMPARABLE A LA STRUCTURE SILICE THERMIQUE - SI (ANALYSE I(V) QUASISTATIQUE). LA DISPERSION EN FREQUENCE DES CARACTERISTIQUES C(V) EST NULLE ET L'ANALYSE TERMAN INDIQUE UN MINIMUM DE DENSITES D'ETATS D'INTERFACE EGAL A 2 10#1#1 CM##2 EV##1